Silver and Silver Alloys Silver possesses the highest electrical and thermal conductivity, low contact resistance, very good deformability and is characterized by good brazability and weldability. Silver as contact material satisfies the requirements only in a narrow range of electrical applications. Alloying of silver with palladium improves the resistance against both the electric wear and corrosion. Alloying of silver with copper and nickel in low concentrations increases the mechanical hardness and the resistance against electrical wear, but without reducing the electrical conductiviy and increasing contact resistance essentially. Finally, silver with alloying additives like manganese and nickel are the basis for dispersion hardened alloys. - Ag
- AgPd30...50
- AgCu3...28
- ARGODUR SPECIAL: AgNi 0,15
- ARGODUR 27: Ag (Cu+Ni) 2
- ARGODUR 32: Ag (Mg+Ni) 0,3...0,5
• Produced by a melting process, extruded, rolled resp. drawn.
• Processing in the shape of rods, wires, strips, profiles, tips and rivets.
^Top
Silver/Nickel SINIDUR Powder metallurgically produced silver/nickel contact materials are more resistant against electric wear and contact welding than silver alloys. They possess good arc mobility and arc extinguishing properties as well as high electrical and thermal conductivity. Contact resistance increases with the amount of nickel. SINIDUR contact materials can be deformed without problems and they are brazable and weldable. - SINIDUR
Ag/Ni 10...40
• Produced powder metallurgically, sintered, rolled resp. drawn.
• Processing in the shape of rods, wires, strips, profiles, tips and rivets.
^Top
Silver/Tin Oxide SISTADOX SISTADOX contact materials are characterized by the following properties: long life time of the contact pieces, low contact resistance, high security against contact welding, good arc mobility and arc extinguishing properties, ecological. SISTADOX contact materials are optimized for different applications and utility categories by adding small amounts of additional metal oxides and applying different production technologies. - SISTADOX P, PW4 and WPW4
Ag/SnO2 8,10 PW4 + 12P and 8...12 WPW4
• Produced powder metallurgically, sintered, extruded, rolled resp. drawn.
SISTADOX P/PW4
• Processing in the shape of rods, wires and rivets.
SISTADOX WPW4
• An additional Ag layer on the underside makes the material brazable and weldable.
• The Ag underside can be provided with a layer of a bazing alloy (e.g. L-Ag15P).
• Processing in the shape of strips, profiles and tips. - SISTADOX PW10
Ag/SnO28...12 PW10
• Produced powder metallurgically, sintered, extruded, rolled resp. drawn.
• With low concentrations of WO3 additives.
• Processing in the shape of rods, wires (wire riveting) and rivets. - SISTADOX PE
Ag/SnO28...12 PE
• Produced powder metallurgically, sintered, extruded, rolled resp. drawn.
• With Bi2O3 - and CuO additives
• Processing in the shape of rods, wires (wire riveting) and rivets. - SISTADOX PX and WPX
Ag/SnO2 2...8 PX and Ag/SnO2 6...14 WPX
• Produced powder metallurgically, based on the reaction spray process,
sintered, extruded, rolled resp. drawn.
• With Bi2O3 - and CuO additives.
SISTADOX PX:
• Ag/SnO2 2 PX wire sections can be welded on directly to the carrier material.
• Processing in the shape of rods, wires (wire riveting) and rivets.
SISTADOX WPX:
• An additional Ag layer on the underside (10-20% of the total thickness)
makes the material brazable and weldable.
• The underside can be provided with a layer of a brazing alloy (e.g. L-Ag15P).
• Processing in the shape of strips, profiles and tips. - SISTADOX PC and WPC
Ag/SnO2 2...8 PC and Ag/SnO2 6...14 WPC
• Produced powder metallurgically, based on the reaction spray process,
sintered, extruded, rolled resp. drawn.
• Comparing to SISTADOXPX and WPX with a higher concentration
of Bi2O3 - and CuO additives.
SISTADOX PC:
• Ag/SnO2 2 PC wire sections can be welded on directly to the carrier material.
• Processing in the shape of rods, wires (wire riveting) and rivets.
SISTADOX WPC:
• An additional Ag layer on the underside (10-20% of the total thickness)
makes the material brazable and weldable.
• The underside can be provided with a layer of a brazing alloy (e.g. L-Ag15P).
• Processing in the shape of strips, profiles and tips. - SISTADOX WPD
Ag/SnO2 6...14 WPD
• Produced powder metallurgically, sintered, extruded, rolled resp. drawn.
• With Ag2MoO4 additives.
• An additional Ag layer on the underside (10-20% of the total thickness)
makes the material brazable and weldable.
• The underside can be provided with a layer of a brazing alloy (e.g. L-Ag15P).
• Processing in the shape of strips, profiles and tips. - SISTADOX TOS F
Ag/SnO2 8...14 TOS F and WTOS F
• Produced melting metallurgically, melting Ag-Sn-In alloys, subsequent, casting and oxidation.
• With In2O3 additives.
• TOS F Processing in the shape of rods, wires and rivets
• WTOS F an additional Ag layer on the underside makes the material brazable and weldable. Processing in the shape strips, profiles and tips.
^Top
Silver/Zinc Oxide DODURIT DODURIT contact materials consists of silver/zinc oxide or silver/cadmium oxide. The ecological DODURITZNO contact materials, and particularly with specific metal oxide additives, are characterized by a high switching life time in AC relay applications. - DODURIT ZNO P
AgZnO 8 P
• Produced powder metallurgically, sintered, extruded, rolled resp. drawn.
• Without additional metal oxides.
• Processing in the shape of rods, wires (wire riveting) and rivets. - DODURIT ZNO WP
AgZnO 8 WP
• Produced powder metallurgically, sintered, extruded, rolled resp. drawn.
• Without additional metal oxides.
• An additional Ag layer on the underside (10-20% of the total thickness)
makes the material brazable and weldable.
• The underside can be provided with a layer of a brazing alloy (e.g. L-Ag15P).
• Processing in the shape of strips, profiles and tips.
- DODURIT ZNO PW25
AgZnO 6...10 PW25
• Produced powder metallurgically with manufacturing procedure "coating",
sintered,
extruded, rolled resp. drawn.
• With Ag2WO4 additives.
• Processing in the shape of rods, wires (wire riveting) and rivets.
- DODURIT ZNO WPW25
Ag/ZnO 6...10 WPW25
• Produced powder metallurgically with manufacturing procedure "coating",
sintered,
extruded,
rolled resp. drawn.
• With Ag2WO4 additives.
• An additional Ag layer on the underside (10-20% of the total thickness)
makes the material brazable and weldable.
• The underside can be provided with a layer of a brazing alloy (e.g. L-Ag15P).
• Processing in the shape of strips, profiles and tips.
^Top
Silver/Cadmium Oxide DODURIT
DODURITcontact materials consists of silver/cadmium oxide or silver/zinc oxide. Cd containing materials are increasingly substitited by ecological SISTADOX or by DODURIT ZnO - contact materials.DODURITCDO is apllied in switchgears when a long life time of the contact pieces, resistance against welding and low contact resistance is demand.
- DODURIT CDO
AgCdO 10...15
• AgCd alloy, casted, extruded, rolled resp. drawn, internal oxidized, drawn.
• Processing in the shape of rods, wires (wire riveting) and rivets. - DODURIT CDO ZH
AgCdO 10...15 ZH
• AgCd alloy, casted, rolled, internal oxidized, rolled resp. drawn.
• The AgCd 10...15 layer on the underside (10-30% of the total thickness)
makes the material brazable and weldable.
• The AgCd 10...15 underlayer can be additionally provided with a layer of\
a brazing alloy (e.g. L-Ag15P).
• Processing in the shape of strips, profiles and tips. - DODURIT CDO AG
AgCdO 10...15 AG
• AgCd alloy, casted, rolled, internal oxidized, rolled resp. drawn.
• An additional Ag layer on the underside (10-20% of the total thickness)
makes the material brazable and weldable.
• The Ag underlayer can be additionally provided with a layer of a brazing alloy
(e.g. L-Ag15P).
• Processing in the shape of strips, profiles and tips. - DODURIT CDO P
AgCdO 10...15 P
• Produced powder metallurgically, sintered, extruded, rolled resp. drawn.
• Processing in the shape of rods, wires (wire riveting) and rivets. - DODURIT CDO WP
AgCdO 10...15 WP
• Produced powder metallurgically, sintered, extruded, rolled resp. drawn.
• An additional Ag layer on the underside (10-20% of the total thickness)
makes the material brazable and weldable.
• The underside can be provided with a layer of a brazing alloy (e.g. L-Ag15P).
• Processing in the shape of strips, profiles and tips.
^Top
Silver/Graphite GRAPHOR GRAPHOR contact materials possesses very high resistance against welding at closing and when contacts are closed in case of short circuits. The welding resistance increases with the concentration of graphite but also the amount of electric wear. GRAPHOR contact materials with graphite fibres embedded into the Ag matrix are improved both regarding to the overtemperature properties and to the switching life time, comparing to conventional silver/graphite materials. - GRAPHOR
Ag/C 2...5
• Produced powder metallurgically, sintered and extruded.
• The graphite particles are aligned vertically to the switching surface.
• Tips on one side or on all sides with a thin Ag layer.
• Welding side is planed or shaped and should the occasion arise, provided
with an additional layer of a brazing alloy (e.g. L-Ag15P).
• Processing in the shape of tips. - GRAPHOR D
Ag/C 3D...4D
• Produced powder metallurgically, sintered, extruded and rolled.
• The graphite particles are aligned parallel to the switching surface.
• Welding side with a thin Ag layer, shaped, and should the occasion arise,
provided with an additional layer or a brazing alloy (e.g. L-Ag15P).
• Processing in the shape of strips and tips. - GRAPHOR DF
Ag/C DF
• Produced powder metallurgically, sintered, extruded and rolled.
• The graphite is embedded into the Ag matrix as powder (approx. 1,5 wt.%)
and in the shape of fibres (approx. 2,3 wt.%).
• Welding side with a thin Ag or AgNi10 layer, shaped, and should the
occasion arise, provided with an additional layer or a brazing alloy (e.g. L-Ag15P).
• Processing in the shape of strips and tips.
^Top
Silver/Tungsten, Silver/Tungsten Carbide SIWODUR These contact materials possess a very high resistance against electric wear and contact welding. Due to the formation of tungsten oxides and tungstates on the surface of silver/tungsten contact materials, contact resistance will increase during the switching life time. Silver/Tungsten Carbide is more favourable in this respect. With a small amount of graphite overtemperature behaviour can be additionally improved. - SIWODUR
Ag/W 50...80 - SIWODUR C
Ag/WC 40...65 • Produced powder metallurgically in single pressed technics, subsequently
infiltrated with Ag in liquid phase.
• The lower side of the contact tips is shaped and infiltrated with a certain excess of Ag.
• The lower side can be additionally provided with a layer of a brazing alloy
(e.g. L-Ag15P).
• Processing in the shape of tips.
^Top
Silver/Molybdenum SILMODUR Silver/molybdenum has a slightly lower electric wear resistance than silver/tungsten. Since molybdenum oxides are less stable than tungsten oxides, the surface of SILMODUR contact pieces can be more easily cleaned by the electric arc and for that reason contact resistance is lower. - SILMODUR
Ag/Mo 50...65
• Produced powder metallurgically in single pressed technics, subsequently
infiltrated with Ag in liquid phase.
• Lower side of the contact tips is shaped and infiltrated with a certain excess of Ag.
• The lower side can be additionally provided with a layer of a brazing alloy
(e.g. L-Ag15P).
• Processing in the shape of tips.
^Top
Copper/Chromium, Copper/Tungsten, Silver/Tungsten Carbide VACURIT VACURIT contact materials, based on copper/chromium, copper/tungsten, copper/tungsten/antimony and silver/tungsten carbide, are optimized for vacuum switches. They have a sufficiently low gas content or only a slight tendency to release gases. The electric wear of VACURIT contact materials during life time is generally flat and uniform. The materials are largely resistant to welding. This applies both to closing and to the conduction of high currents. Both, contact resistance and copping current, of VACURIT contact materials remain largely unchanged throughout the service life of the switching device. - VACURIT
Cu/Cr 25...50 - VACURIT
W/Cu 20, W/Cu30/Sb1 - VACURIT
WC/Ag 40• Produced powder metallurgically in single pressed technics,
sintered and if necessary additionally pressed.
• WC/Ag is infiltrated by Ag in liquid phase, after pressing the powder and sintering.
• Processing iin the shape of discs, rings, mouldings spirally and radially slitted.
^Top
Copper/Tungsten CUWODUR CUWODUR contact materials consist of copper/tungsten and copper/tungsten carbide. This group of materials is especially arc and electric wear resistant and is used in high and medium voltage switchgears. In these applications CUWODUR shows its high resistance to thermal and mechanical shocks. An additional field of application of CUWODUR materials are electrodes for lighting protection devices. - CUWODUR
Cu/W 50...80 - CUWODUR H
Cu/W 75H...80H - CUWODUR C
Cu/WC 50• Produced powder metallurgically in single pressed technics,
sintered and infiltrated with Cu in liquid phase.
• Joining of CUWODUR materials with electrically and thermally high conductive
carrier materials by electron beam welding, percussion welding and brazing.
• Processing in the shape of tips, formed parts, tuplis, spring hard tulips, tubes and rods.
^Top |